Styrene-Butadiene Rubber (SBR)
Product List
Non-Oil Based:
- SBR 1500
- SBR 1502
- SBR 1507
Oil-Based:
- SBR 1712
- SBR 1723
Description
Styrene-Butadiene Rubber is produced by a technology of cold emulsion copolymerization based on soaps of rosin and fatty acids and contains 23.5% of chemically bonded styrene. It is coagulated by a system of acid and synthetic coagulant.
SBR has very good properties such as process ability, abrasion resistance, less tendency to scorching processing. More than half of the world production of E-SBR is used principally in general-purpose tires.
The products are available in clear or oil-extended grades, with staining or non-staining antioxidant.
Packing
- 1 Bale, wrapped in polyethylene film = 35 kg
- 1 Pallet (36 Bales) = 1.26 MT ±18 kg
- 1 Container (19 Pallets), 40-ft FCL = 23.94 MT

Parameters | Units | Values | Test methods |
---|---|---|---|
Mooney viscosity (ML 1+4 @ 100 oC)
|
MU
|
46-58
|
ASTM D1646
|
Mooney viscosity (ML 1+4 @ 100 oC) 2
|
MU
|
<84
|
ASTM D1646
|
Volatile matters
|
% wt.
|
< 0.75
|
ASTM D5668
|
Total ash
|
% wt.
|
< 1.5
|
ASTM D5667
|
Organic acids
|
% wt.
|
4.75 -7.5
|
ASTM D5774
|
Soaps
|
% wt.
|
< 0.5
|
ASTM D5774
|
Bounded styrene
|
% wt.
|
22.5-24.5
|
ASTM D5775
|
Tensile strength(35 min cured)2
|
kg/cm2
|
>250
|
ASTM D 412
|
Ultimate elongation(35 min cured)2
|
%
|
>470
|
ASTM D 412
|
300 % Modulus(35 min cured)2
|
kg/cm2
|
119-159
|
ASTM D 412
|
Parameters | Units | Values | Test methods |
---|---|---|---|
Mooney viscosity (ML 1+4 @ 100 oC)
|
MU
|
46-58
|
ASTM D1646
|
Mooney viscosity (ML 1+4 @ 100 oC) 2
|
MU
|
<84
|
ASTM D1646
|
Volatile matters
|
% wt.
|
< 0.75
|
ASTM D5668
|
Total ash
|
% wt.
|
< 1.5
|
ASTM D5667
|
Organic acids
|
% wt.
|
4.75 -7.5
|
ASTM D5774
|
Soaps
|
% wt.
|
< 0.5
|
ASTM D5774
|
Bounded styrene
|
% wt.
|
22.5-24.5
|
ASTM D5775
|
Tensile strength(35 min cured)2
|
kg/cm2
|
>250
|
ASTM D 412
|
Ultimate elongation(35 min cured)2
|
%
|
>350
|
ASTM D 412
|
300 % Modulus(35 min cured)2
|
kg/cm2
|
167-207
|
ASTM D 412
|
Parameters | Units | Values | Test methods |
---|---|---|---|
Mooney viscosity (ML 1+4 @ 100 oC)
|
MU
|
30-40
|
ASTM D1646
|
Mooney viscosity (ML 1+4 @ 100 oC) 2
|
MU
|
<67
|
ASTM D1646
|
Volatile matters
|
% wt.
|
< 0.75
|
ASTM D5668
|
Total ash
|
% wt.
|
< 1.5
|
ASTM D5667
|
Organic acids
|
% wt.
|
4.75 -7.5
|
ASTM D5774
|
Soaps
|
% wt.
|
< 0.5
|
ASTM D5774
|
Bounded styrene
|
% wt.
|
22 – 25
|
ASTM D5775
|
Tensile strength(35 min cured)2
|
kg/cm2
|
>240
|
ASTM D 412
|
Ultimate elongation(35 min cured)2
|
%
|
160 – 200
|
ASTM D 412
|
300 % Modulus(35 min cured)2
|
kg/cm2
|
160 – 200
|
ASTM D 412
|
Parameters | Units | Values | Test methods |
---|---|---|---|
Mooney viscosity (ML 1+4 @ 100 oC)
|
MU
|
42 – 52
|
ASTM D1646
|
Mooney viscosity (ML 1+4 @ 100 oC)-compound 2
|
MU
|
<67
|
ASTM D1646
|
Volatile matters
|
% wt.
|
< 0.75
|
ASTM D5668
|
Total ash
|
% wt.
|
< 1.5
|
ASTM D5667
|
Organic acids
|
% wt.
|
3.9 – 5.7
|
ASTM D5774
|
Soaps
|
% wt.
|
< 0.5
|
ASTM D5774
|
Bounded styrene
|
% wt.
|
22.5 – 24.5
|
ASTM D5775
|
Oil Content
|
% wt.
|
25.8 – 28.8
|
ASTM D 1416
|
Tensile strength(35 min cured)2
|
kg/cm2
|
>200
|
ASTM D 412
|
Ultimate elongation(35 min cured)2
|
%
|
>530
|
ASTM D 412
|
300 % Modulus(35 min cured)2
|
kg/cm2
|
79 – 109
|
ASTM D 412
|
SBR 1723
Parameters | Units | Values | Test methods |
---|---|---|---|
Mooney viscosity (ML 1+4 @ 100 oC)
|
MU
|
42 – 52
|
ASTM D1646
|
Mooney viscosity (ML 1+4 @ 100 oC)-compound 2
|
MU
|
<62
|
ASTM D1646
|
Volatile matters
|
% wt.
|
< 0.75
|
ASTM D5668
|
Total ash
|
% wt.
|
< 1
|
ASTM D5667
|
Organic acids
|
% wt.
|
3.9 – 5.7
|
ASTM D5774
|
Soaps
|
% wt.
|
< 0.5
|
ASTM D5774
|
Bounded styrene
|
% wt.
|
22.5- 24.5
|
ASTM D5775
|
Oil Content
|
% wt.
|
24 – 29
|
ASTM D 1416
|
Tensile strength(35 min cured)2
|
kg/cm2
|
>200
|
ASTM D 412
|
Ultimate elongation(35 min cured)2
|
%
|
>530
|
ASTM D 412
|
300 % Modulus(35 min cured)2
|
kg/cm2
|
79 – 109
|
ASTM D 412
|